Synthesis of silver nanoparticlesMicroemulsion techniques

Uniform and size controllable silver NPs can be synthesized using microemulsion techniques. The NPs preparation in two-phase aqueous organic systems is based on the initial spatial separation of reactants (metal precursor and reducing agent) in two immiscible phases. The interface between the two liquids and the intensity of inter-phase transport between two phases, which is mediated by a quaternary alkyl-ammonium salt, affect the rate of interactions between metal precursors and reducing agents. Metal clusters formed at the interface are stabilized, due to their surface being coated with stabilizer molecules occurring in the non-polar aqueous medium, and transferred to the organic medium by the inter-phase transporter (38). One of the major disadvantages is the use of highly deleterious organic solvents.

Thus large amounts of surfactant and organic solvent must be separated and removed from the final product. For instance, Zhang and coworkers (39) used dodecane as oily phase (a low deleterious and even nontoxic solvent), but there was no need to separate the prepared silver solution from the reaction mixture. On the other hand, colloidal NPs prepared in nonaqueous media for conductive inks are well-dispersed in a low vapor pressure organic solvent, to readily wet the surface of polymeric substrate without any aggregation. The advantages can also be found in the applications of metal NPs as catalysts to catalyze most organic reactions, which have been conducted in non-polar solvents. It is very important to transfer metal NPs to different physicochemical environments in practical applications (40).


Home | About Us | Products | News | Exhibition | Contact Us | Feedback | Mobile | XML

TEL: +86-757-8128-5193  E-mail: chinananomaterials@aliyun.com

Copyright © Guangdong Nanhai ETEB Technology Co.,Ltd All rights reserved.